Add to your list(s)
Download to your calendar using vCal
If you have a question about this talk, please contact Emli-Mari Nel.
Thermal contraction over a large temperature range is explained by a geometrical effect due to beta-eucryptite’s framework structure, which is roughly independent of phonon frequency, and mitigated by a positive contribution due to anharmonicity, which decreases with increasing frequency.